The dry mixed plastering mortar is mainly composed of high-quality cement as the main bonding material, accurately screened and prepared river sand, combined with high-quality water retaining and thickening materials, accurately measured dry mixing agent, and mixed with a dual axis forced mixer. It is a specialized improved dry powder designed and manufactured with high-quality polymer, and can be used only by adding water on site and mechanically stirring according to requirements. Water retention rate is a very important indicator, so what is the impact of water retention rate on dry mixed plastering mortar? Below, Jinan plastering mortar manufacturer will analyze for you:

一、保水性差會(huì)導(dǎo)致塑性開裂；砂漿保水性差，水分容易流失，尤其是對(duì)于吸水快的加氣塊墻，水分被基材吸走，而干混抹灰砂漿沒有凝結(jié)，無法抵抗體積收縮引起的拉應(yīng)力，導(dǎo)致出現(xiàn)不規(guī)則裂紋。

1、 Poor water retention can lead to plastic cracking; Mortar has poor water retention and is prone to water loss, especially for aerated block walls that absorb water quickly. Water is absorbed by the substrate, while dry mixed plastering mortar does not set and cannot resist tensile stress caused by volume shrinkage, resulting in irregular cracks.

二、保水率差，會(huì)造成空鼓；干混抹灰砂漿泌水會(huì)造成砂漿成分不均勻，導(dǎo)致整體性能下降。對(duì)于干混抹灰砂漿，水分流失快，容易被基材奪走，水泥水化不充分，降低了砂漿與基材的粘結(jié)力。隨著溫度和濕度的變化，砂漿會(huì)發(fā)生體積變形，形成應(yīng)力，導(dǎo)致砂漿與基材分離。這種現(xiàn)象是砂漿空鼓的主要原因。

2、 Poor water retention rate can cause hollowing; The bleeding of dry mixed plastering mortar can cause uneven mortar composition, leading to a decrease in overall performance. For dry mixed plastering mortar, water loss is fast, it is easy to be taken away by the substrate, and the cement hydration is insufficient, reducing the bonding force between the mortar and the substrate. With changes in temperature and humidity, the mortar will undergo volume deformation, forming stress, leading to separation between the mortar and the substrate. This phenomenon is the main cause of mortar hollowing.

三、保水性差，施工性差；干混抹灰砂漿的保水性差，會(huì)產(chǎn)生砂漿泌水，砂漿在加水?dāng)嚢韬蟮倪\(yùn)輸過程中或放置過程中，會(huì)產(chǎn)生分層與上、中、底層稠度不同，造成粘結(jié)性差，抹灰易落灰，砂漿操作性差等后果。

3、 Poor water retention and construction performance; The poor water retention of dry mixed plastering mortar can result in mortar bleeding. During the transportation or placement process after mixing with water, the mortar will have different layers and the consistency of the upper, middle, and bottom layers, resulting in poor adhesion, easy falling of the plaster, and poor operability of the mortar.

那么今天的講解就先到這里了，以上就是今天的全部?jī)?nèi)容，相信大家對(duì)保水率對(duì)干混抹灰砂漿的影響也有了一定的認(rèn)識(shí)。非常感謝您的耐心閱讀。如還想了解更多關(guān)于干混抹灰砂漿的相關(guān)問題，您可以關(guān)注我們網(wǎng)站http://m.netjobs.cc咨詢！

So that's all for today's explanation. That's all for today. I believe everyone has a certain understanding of the impact of water retention rate on dry mixed plastering mortar. Thank you very much for your patience in reading. If you want to learn more about dry mixed plastering mortar, you can follow our website http://m.netjobs.cc consulting service